UNS S45500 Hardened
Equivalent material: DIN 1.4543, DIN X3CrNiCuTi12-9, DIN X3CrNiCuTiNb12-9, AISI S45500, AISI XM-16, SAE S45500, SAE XM-16, EN 1.4543, ASTM XM-16
UNS S45500 Hardened general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
UNS S45500 Hardened thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
UNS S45500 Hardened electrical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.05 % |
| Chromium |
Chromium of 11 - 12.5 % |
| Copper |
Copper of 1.5 - 2.5 % |
| Iron |
Iron of 71.5 - 79.2 % |
| Manganese |
Manganese of 0 - 0.5 % |
| Molybdenum |
Molybdenum of 0 - 0.5 % |
| Nickel |
Nickel of 7.5 - 9.5 % |
| Niobium |
Niobium of 0 - 0.5 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Silicon |
Silicon of 0 - 0.5 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
| Tantalum |
Tantalum of 0 - 0.5 % |
| Titanium |
Titanium of 0.8 - 1.4 % |
UNS S45500 Hardened mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 9.2 - 12 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 1630 - 1860 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 1470 - 1740 MPa |
- |