UGIMA® 4006/UGI® 4006 introduction
Martensitic grade combining high mechanical properties with good corrosion resistance on suitably polished surfaces in moderately aggressive non-chlorinated environments (optimum in treated state) Good resistance in oxidizing atmosphere up to 600°C. UGIMAR grade produced according to an Ugitech process to significantly improve its machinability (15% to 25% increase in productivity), up to diameter 115 mm
Equivalent material: EN 1.4006, EN X12Cr13, DIN 1.4006, DIN X12Cr13, AISI 410
- DIN 17440 Grade X10Cr13 quenched and tempered (+QT)
- DIN 1654-5 Grade X10Cr13 quenched and tempered (+QT)
- DIN 1654-5 Grade X10Cr13 annealed to achieve spheroidized carbides (+AC)
- DIN 1654-5 Grade X10Cr13 annealed to achieve spheroidized carbides, cold worked (+AC+C)
- DIN 1654-5 Grade X10Cr13 cold drawn, annealed to achieve spheroidized carbides and slightly skin passed
- ASTM A268 Grade TP410 Reheated
- ASTM A426 Grade CPCA15 Austenitized and Tempered
- ASTM A479 Grade 410 Annealed
- ASTM A479 Grade 410 1
- ASTM A479 Grade 410 2
UGIMA® 4006/UGI® 4006 general
| Property | Value | Comment |
|---|---|---|
| Carbon | Carbon of 0.12 % | - |
| Chromium | Chromium of 12.5 % | - |
| Sulfur | Sulfur of 0.03 | max. |
UGIMA® 4006/UGI® 4006 mechanical
| Property | - | - | |||
|---|---|---|---|---|---|
| Application areas | |||||
| Corrosion properties | |||||
| Heat Treatment | |||||
| Other | Product | Shape | Finish | Tolerance | Dimensions |
| Bar | Round | Rolled and descaled bars | 12 to 13 | 22 to 15 mm | |
| - | Round | Turned and polished | 9 to 11 | 22 to 115 mm | |
| - | Round | Drawn bar | 8 to 9 | 3 to 55 mm | |
| - | Round | Ground bar | 6 to 9 | 3 to 80 mm | |
| - | Hexagonal | Drawn bar | 11 | 3 to 55 mm | |
| Wire rod | Round | Pickled | - | 5.0 to 32 mm | |
| Drawn wire | Round | - | - | 16.0 to 1.0 mm |