Steel C45E is suitable for mean loaded parts of higher dimensions (large forged parts) and more complex form in vehicle manufacturing and machine engineering (e.g. shipshafts, transmission parts, wheel hubs). Lowest working temperature -25 °C, favorable creep behavior up to 480 °C. As a bright ste ...
Equivalent material: NBN C45-2, GB 45, AFNOR XC48H1, BS 080M46, ISO C45E4, UNI C45, JIS S45C, SS 1672, UNE F1140-C45K, ASTM 1045Steel C35E is suitable for slightly higher loaded components with higher dimensions (large forged parts) and more complex form as well as higher demands on uniformity of qualities and surface appearance in vehicle manufacturing and machine engineering (e.g. transmissin parts, crankshafts). As a bri ...
Equivalent material: GB 35, GB U20352, IS 35C8, ISO C35E, JIS S35C, KS SM35C, GOST 35, ASTM A29 Grade 1035, ASTM A510 Grade 1035, ASTM A576 Grade 1035Steel C25 is suitable for low strained parts of small heat-treatment sections in vehicle manufacturing and machine engineering (e.g. gear wheels, piston rods). Lowest working temperature -25 °C. ...
Equivalent material: NBN C25-1, BS 070M26, GOST 25, ISO C25, UNI C25, PN 25, ASTM 1025, DIN C25, GB 25, GB U20252Steel C22 is suitable for slightly loaded parts of small heat-treatment sections in vehicle manufacturing and machine engineering (e.g. piston rods, gear wheels). Lowest working temperature -25 °C. ...
Equivalent material: AFNOR AF42C20, BS 070M20, GOST 20, UNI C20, JIS S25C, PN 20, ASTM 1020, DIN C22, DIN 1.0402, AFNOR C22Steel C25R is suitable for low strained parts in vehicle manufacturing and machine engineering which have to meet higher demands on workability while maintaining mechanical properties (e.g. transmission parts, crankshafts, cylinder). Lowest working temperature -25 °C. ...
Equivalent material: NBN C25-3, AFNOR XC25u, BS 070M26, ISO C25M2, UNE F1125-C25K-1, ASTM 1025, DIN Cm25, GB 25, GB U20252, EN 1.1163Steel C25E is suitable for low strained parts of higher dimension and more complex form as well as higher demands on uniformity of proprties and surface appearance (e.g. transmission parts, crankshafts). Lowest working temperature -25 °C. ...
Equivalent material: NBN C25-2, GB 25, AFNOR XC25, BS 070M26, ISO C25E4, UNI C25, UNE F1120-C25K, ASTM 1025, ASTM C, DIN Ck25Boron-alloyed tempering steel for general machine engineering. The steel is shearable in the non-treated condition. ...
Equivalent material: EN 1.5531, IS 30MnB5, DIN 1.5531, EN 23MnB4, DIN 23MnB4, DIN 30MnB5, AFNOR 30MnB5, UNI 30MnB5, UNE 30MnB5, JIS SWRCHB634Boron-alloyed tempering steel for general machine engineering and vehicle manufacturing. The steel is shearable in the non-treated condition. ...
Equivalent material: EN 1.5530, IS 20MnB5, DIN 21MnB5, DIN 1.5530, DIN 20MnB5, UNI 20MnB5, UNI 21B3, UNE 20MnB5, UNE 21B3, BS 174H20