Sandvik 8R41
Sandvik 8R41 introduction
Sandvik 8R41 is a niobium-stabilized austenitic stainless steel.
Datasheet URL:
Sandvik 8R41
Datasheet updated 2017-01-19 12:22 (supersedes all previous editions)
Equivalent material: EN 1.4961, EN X8CrNiNb16-13, DIN 1.4961, DIN X8CrNiNb16-13
Sandvik 8R41 general
| Property |
Value |
Comment |
| Recycled Content |
Recycled Content of 82.1 % |
Average recycled content |
Sandvik 8R41 thermal
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.06 % |
max. |
| Chromium |
Chromium of 16.5 % |
- |
| Iron |
- |
| Manganese |
Manganese of 1.3 % |
- |
| Nickel |
Nickel of 13 % |
- |
| Niobium |
Niobium of 0.7 % |
- |
| Phosphorus |
Phosphorus of 0.02 % |
max. |
| Silicon |
Silicon of 0.4 % |
- |
| Sulfur |
Sulfur of 0.015 % |
max. |
Sandvik 8R41 mechanical
| Property |
Temperature |
Value |
Comment |
| Elongation |
23.0 °C |
Elongation of 35 % |
min. |
| Tensile strength |
23.0 °C |
Tensile strength of 510 - 690 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
min. |