Sandvik 6LR62

Sandvik 6LR62 introduction

Sandvik 6LR62 is a molybdenum-alloyed austenitic stainless steel.

Datasheet URL:
Sandvik 6LR62

Datasheet updated 2019-09-04 08:01 (supersedes all previous editions)

Equivalent material: UNS S31600, UNS S31609, ASTM TP316, ASTM TP316H, EN 1.4401, DIN 1.4401, AFNOR Z6ZND17-12, EN X5CrNiMo17-12-2

Sandvik 6LR62 general

Property	Value	Comment
Recycled Content	Recycled Content of 82.1 %	Average recycled content

Sandvik 6LR62 thermal

Property	Value	Comment
Carbon	Carbon of 0.05 %	min.
Chromium	Chromium of 17 %	-
Iron	-
Manganese	Manganese of 1.5 %	-
Molybdenum	Molybdenum of 2.1 %	-
Nickel	Nickel of 11.5 %	-
Phosphorus	Phosphorus of 0.04 %	max.
Silicon	Silicon of 0.6 %	-
Sulfur	Sulfur of 0.015 %	max.

Sandvik 6LR62 electrical

Property	-	-
Welding

Sandvik 6LR62 mechanical

Property	Temperature	Value	Comment
Creep strength 10^4 cycles	550.0 °C	Creep strength 10^4 cycles of 255 MPa	ISO values, at 10000h
-	575.0 °C	Creep strength 10^4 cycles of 214 MPa	ISO values, at 10000h
-	600.0 °C	Creep strength 10^4 cycles of 172 MPa	ISO values, at 10000h
-	625.0 °C	Creep strength 10^4 cycles of 137 MPa	ISO values, at 10000h
-	650.0 °C	Creep strength 10^4 cycles of 108 MPa	ISO values, at 10000h
-	675.0 °C	Creep strength 10^4 cycles of 83 MPa	ISO values, at 10000h
-	700.0 °C	Creep strength 10^4 cycles of 64 MPa	ISO values, at 10000h
-	725.0 °C	Creep strength 10^4 cycles of 49 MPa	ISO values, at 10000h
-	750.0 °C	Creep strength 10^4 cycles of 37 MPa	ISO values, at 10000h
Creep strength 10^5 cycles	550.0 °C	Creep strength 10^5 cycles of 177 MPa	ISO values, at 100000h
-	575.0 °C	Creep strength 10^5 cycles of 137 MPa	ISO values, at 100000h
-	600.0 °C	Creep strength 10^5 cycles of 108 MPa	ISO values, at 100000h
-	625.0 °C	Creep strength 10^5 cycles of 86 MPa	ISO values, at 100000h
-	650.0 °C	Creep strength 10^5 cycles of 64 MPa	ISO values, at 100000h
-	675.0 °C	Creep strength 10^5 cycles of 46 MPa	ISO values, at 100000h
-	700.0 °C	Creep strength 10^5 cycles of 33 MPa	ISO values, at 100000h
-	725.0 °C	Creep strength 10^5 cycles of 25 MPa	ISO values, at 100000h
-	750.0 °C	Creep strength 10^5 cycles of 18 MPa	ISO values, at 100000h
Elongation	23.0 °C	Elongation of 45 %	min.
Tensile strength	23.0 °C	Tensile strength of 515 - 790 MPa	-
Yield strength Rp0.2	20.0 °C	Yield strength Rp0.2 of 205 MPa	min.
-	50.0 °C	Yield strength Rp0.2 of 196 MPa	min.
-	100.0 °C	Yield strength Rp0.2 of 175 MPa	min.
-	150.0 °C	Yield strength Rp0.2 of 158 MPa	min.
-	200.0 °C	Yield strength Rp0.2 of 145 MPa	min.
-	250.0 °C	Yield strength Rp0.2 of 135 MPa	min.
-	300.0 °C	Yield strength Rp0.2 of 127 MPa	min.
-	350.0 °C	Yield strength Rp0.2 of 120 MPa	min.
-	400.0 °C	Yield strength Rp0.2 of 115 MPa	min.
-	450.0 °C	Yield strength Rp0.2 of 112 MPa	min.
-	500.0 °C	Yield strength Rp0.2 of 110 MPa	min.
-	550.0 °C	Yield strength Rp0.2 of 108 MPa	min.