SAE J404 Grade 1345
Equivalent material: DIN 1.0919, DIN H220BD, DIN HX220BD, AFNOR HX220BD, BS HX220BD, AISI 1345, JIS JSC340H, EN HX220BD, EN H220BD, EN 1.0919, GB 45Mn2, GB/T HX220BD, ASTM 1345, DIN 1.0912, DIN 46Mn7, AISI 1345H, SAE 1345H, JIS SMn443M, JIS SMn443TK, EN 1.0912, GOST 45G2, UNS H13450, UNS G13450
- JIS G3106 Grade SM400C
- JIS G3115 Grade SPV315
- JIS G3115 Grade SPV355
- JIS G3106 Grade SM400B
- JIS G3106 Grade SM400A
- JIS G3116 Grade SG295
- EN 10292 Grade HX220BD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated
- EN 10292 Grade HX220BD hot rolled or cold rolled, hot dip coated,+Z, +ZF, +ZA, +AZ, +AS
- ASTM A752 Grade 1345 Annealed
- JIS G3311 Grade SMn443M cold-rolled
SAE J404 Grade 1345 general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for Manganese Steel |
SAE J404 Grade 1345 thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.33E-5 1/K | Typical for Manganese Steel |
| Melting point | - | Melting point of 1382 - 1529 °C | Typical for Manganese Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 510 - 553 J/(kg·K) | Typical for Manganese Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 14 - 16 W/(m·K) | Typical for Manganese Steel |
SAE J404 Grade 1345 electrical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.43 - 0.48 % |
| Manganese | Manganese of 1.6 - 1.9 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.15 - 0.35 % |
| Sulfur | Sulfur of 0.04 % |
SAE J404 Grade 1345 mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Manganese Steel |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Manganese Steel |