SAE J403 Grade 1215
Equivalent material: DIN 1.0736, DIN 9SMn36, DIN 11SMn37, AFNOR 11SMn37, AFNOR S300, BS 11SMn37, AISI 1215, JIS SUM25, JIS 12SMn35, EN 11SMn37, EN 1.0736, ISO 12SMn35, ISO 11SMn37, ASTM 1215, UNS G12150, DIN 1.0715, DIN 9SMn28, DIN 11SMn30, AFNOR S250, AFNOR 11SMn30, BS 230M07, BS 11SMN30, BS 220M07, UNI CF9SMn28, UNI 9SMn23, SS 1912, UNE 11SMn28, AISI 1213, SAE 1213, JIS SUM22, JIS 11SMn28, JIS SUM23, EN 11SMn30, EN 1.0715, ISO 11SMn28, ISO 11SMn30, GB/T U71152, GB/T Y15, UNS G12130, DIN 1.0718, DIN 9SMnPb28, DIN 11SMnPb30, AFNOR S250Pb, AFNOR 11SMnPb30, BS 11SMnPb30, UNI CF9SMnPb28, SS 1914, UNE 11SMnPb28, AISI 12L13, AISI 12L14, SAE 12L13, SAE 12L14, JIS SUM22L, JIS SUM23L, JIS SUM24L, JIS 11SMnPb28, EN 11SMnPb30, EN 1.0718, ISO 11SMnPb30, ISO 11SMnPb28, GB/T U72152, GB/T Y15Pb, UNS G12144, UNS G12134
SAE J403 Grade 1215 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
SAE J403 Grade 1215 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
SAE J403 Grade 1215 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.09 % |
| Chromium |
Chromium of 0.02 % |
| Copper |
Copper of 0.02 % |
| Iron |
balance |
| Manganese |
Manganese of 0.75 - 1.05 % |
| Molybdenum |
Molybdenum of 0.02 % |
| Nickel |
Nickel of 0.02 % |
| Niobium |
Niobium of 0.08 % |
| Phosphorus |
Phosphorus of 0.04 - 0.09 % |
| Silicon |
Silicon of 0.02 % |
| Sulfur |
Sulfur of 0.26 - 0.35 % |
| Titanium |
Titanium of 0.08 % |
| Vanadium |
Vanadium of 0.08 % |
SAE J403 Grade 1215 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
SAE J403 Grade 1215 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
SAE J403 Grade 1215 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |