SAE J1268 Grade 6150H
Equivalent material: DIN 1.8159, DIN GS-50CrV4, DIN 50CrV4, DIN G51CrV4, DIN 51CrV4, AFNOR 50CrV4, BS 735A50, BS 50CrV4, UNI 50CrV4, SS 2230, AISI 6150, AISI 6150H, SAE 6150, JIS SUP10, JIS SUP10M, EN 50CrV4, EN 51CrV4, EN 1.8159, GOST 50HFA, GOST 50HGFA, GB 50CrV4, ASTM A752 Grade 6150, ASTM A304 Grade 6150H, ASTM A231 Grade 6150, ASTM A322 Grade 6150
SAE J1268 Grade 6150H general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Vanadium Steel |
SAE J1268 Grade 6150H thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
Typical for Chromium Vanadium Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Vanadium Steel |
SAE J1268 Grade 6150H electrical
| Property |
Value |
| Carbon |
Carbon of 0.47 - 0.54 % |
| Chromium |
Chromium of 0.75 - 1.2 % |
| Copper |
Copper of 0.35 % |
| Iron |
balance |
| Manganese |
Manganese of 0.6 - 1 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.25 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.04 % |
| Vanadium |
Vanadium of 0.15 % |
SAE J1268 Grade 6150H mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Vanadium Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Vanadium Steel |