SAE J1268 Grade 5135H
Equivalent material: DIN 1.7034, DIN 37Cr4, AFNOR 37Cr4, BS 37Cr4, AISI 5132, AISI 5135H, SAE 5132, JIS SCr435, JIS SCr435WCH, JIS SCr435H, JIS SCr435M, JIS SCr435HRCH, EN 37Cr4, EN 1.7034, GOST 35X, GOST 38ChA, GOST SchCh10, ASTM 5135, UNS H51350, UNS G51320, DIN 1.7038, DIN 37CrS4, AFNOR 37CrS4, BS 37CrS4, EN 37CrS4, EN 1.7038
SAE J1268 Grade 5135H general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Steel |
SAE J1268 Grade 5135H thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.4E-6 - 1.5E-5 1/K |
Typical for Chromium Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 - 494 J/(kg·K) |
Typical for Chromium Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 23 - 50 W/(m·K) |
Typical for Chromium Steel |
SAE J1268 Grade 5135H electrical
| Property |
Value |
| Carbon |
Carbon of 0.32 - 0.38 % |
| Chromium |
Chromium of 0.7 - 1.15 % |
| Copper |
Copper of 0.35 % |
| Iron |
balance |
| Manganese |
Manganese of 0.5 - 0.9 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.25 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.04 % |
SAE J1268 Grade 5135H mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Steel |