SAE J1268 Grade 5132H
Equivalent material: DIN 1.7033, DIN 34Cr4, AFNOR 32C4, BS 530A32, SS 34Cr4(KB), UNE 35Cr4, AISI 5132, AISI 5132H, SAE 5132, JIS SCr430, JIS SCr430WCH, JIS SCr430H, EN 34Cr4, EN 1.7033, GOST 35Ch, GB/T 35Cr, GB/T A20352, UNS H51320, UNS G51320, DIN 1.7037, DIN 34CrS4, AFNOR 34CrS4, BS 34CrS4, EN 34CrS4, EN 1.7037, GOST 30X
SAE J1268 Grade 5132H general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Steel |
SAE J1268 Grade 5132H thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.4E-6 - 1.5E-5 1/K |
Typical for Chromium Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 - 494 J/(kg·K) |
Typical for Chromium Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 23 - 50 W/(m·K) |
Typical for Chromium Steel |
SAE J1268 Grade 5132H electrical
| Property |
Value |
| Carbon |
Carbon of 0.29 - 0.35 % |
| Chromium |
Chromium of 0.65 - 1.1 % |
| Copper |
Copper of 0.35 % |
| Iron |
balance |
| Manganese |
Manganese of 0.5 - 0.9 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.25 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.04 % |
SAE J1268 Grade 5132H mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Steel |