SAE J1268 Grade 1330H
Equivalent material: DIN 1.1170, DIN 28Mn6, DIN ETG 25, AFNOR 28Mn6, AFNOR 20M5, BS 26Mn6, BS En14A, BS En14B, BS 150M19, AISI 1330H, AISI 1527, AISI 1330, AISI 1524, SAE 1527, SAE 1330, SAE 1524, JIS S33C, JIS SCMn1A, JIS SCMn1B, JIS SCMn1, EN 28Mn6, EN 1.1170, ISO 28Mn6, GOST 30G2, GB 30Mn2, GB A00302, GB/T 30Mn2, GB/T A00302, UNS H13300, UNS G13300, IS 20Mn2, IS 20C15
SAE J1268 Grade 1330H general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Manganese Steel |
SAE J1268 Grade 1330H thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.33E-5 1/K |
Typical for Manganese Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Manganese Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 510 - 553 J/(kg·K) |
Typical for Manganese Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 16 W/(m·K) |
Typical for Manganese Steel |
SAE J1268 Grade 1330H electrical
| Property |
Value |
| Carbon |
Carbon of 0.27 - 0.33 % |
| Chromium |
Chromium of 0.2 % |
| Copper |
Copper of 0.35 % |
| Iron |
balance |
| Manganese |
Manganese of 1.45 - 2.05 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.25 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.04 % |
SAE J1268 Grade 1330H mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Manganese Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Manganese Steel |