JIS G5131 Grade SCMnH11

Equivalent material: GOST 110Г13Л, AS H1A, AS H19, NF Z120M12, BS BW10, UNI GX120Mn12, UNI 120Mn13, UNE AM-X120Mn12, UNE AM-X120MnCr12-2, UNE F.240.A(f), UNE F.240.A(1), SIS 2183-02, SIS 2183, ASTM A, JIS SCMnH1, JIS SCMnH2, JIS SCMnH3, GB/T ZGMn13-1, GB/T ZGMn13-2, GB/T ZGMn13-3, GB/T ZGMn13-4, ASTM B-2, ASTM B-3, ASTM B-4

JIS G5131 Grade SCMnH11 general

Property Temperature Value Comment
Density 23.0 °C Density of 7.8 - 7.9 g/cm³ Typical for Manganese Steel

JIS G5131 Grade SCMnH11 thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.33E-5 1/K Typical for Manganese Steel
Melting point - Melting point of 1382 - 1529 °C Typical for Manganese Steel
Specific heat capacity 23.0 °C Specific heat capacity of 510 - 553 J/(kg·K) Typical for Manganese Steel
Thermal conductivity 23.0 °C Thermal conductivity of 14 - 16 W/(m·K) Typical for Manganese Steel

JIS G5131 Grade SCMnH11 mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 200 - 215 GPa Typical for Manganese Steel
Elongation A5 23.0 °C Elongation A5 of 20 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Manganese Steel
Tensile strength 23.0 °C Tensile strength of 740 MPa -
Yield strength Rp0.2 23.0 °C Yield strength Rp0.2 of 390 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us