JIS G4801 Grade SUP10

Equivalent material: GB/T 50CrVA, GB 50CrVA, GOST 50HGA, GOST 50HGFA, GOST 50ChF, GOST 50ChFA, AS 6150, AS 6150H, AS En47, EN 51CrV4, DIN 50CrV4, NF 50CV4, BS 735A51, BS 735H51, IS 50Cr1V23, UNI 50CrV4, UNE F.143, UNE F.143.A, UNE F.1430, UNE 51CrV4, SIS 2230, SIS 2230-00, SIS 2230-02, SIS 2230-03, SIS 2230-04, SIS 2230-05, SIS 2230-06, AMS 6448, AMS 6450, AMS 7301, ASTM 6150, MIL S-8503, AISI 6150, SAE 6150, ASTM 6150H, AISI 6150H, SAE 6150H, DIN 1.8159, DIN GS-50CrV4, DIN G51CrV4, DIN 51CrV4, AFNOR 50CrV4, BS 735A50, BS 50CrV4, SS 2230, JIS SUP10M, EN 50CrV4, EN 1.8159, GOST 50HFA, GB 50CrV4

JIS G4801 Grade SUP10 general

Property Temperature Value Comment
Density 23.0 °C Density of 7.8 - 7.9 g/cm³ Typical for Chromium Vanadium Steel

JIS G4801 Grade SUP10 thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.2E-5 1/K Typical for Chromium Vanadium Steel
Melting point - Melting point of 1382 - 1529 °C Typical for Chromium Vanadium Steel

JIS G4801 Grade SUP10 mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 200 - 215 GPa Typical for Chromium Vanadium Steel
Elongation A5 23.0 °C Elongation A5 of 10 % -
Hardness, Brinell 23.0 °C Hardness, Brinell of 363 - 429 [-] -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Chromium Vanadium Steel
Reduction of area 23.0 °C Reduction of area of 30 % -
Tensile strength 23.0 °C Tensile strength of 1226 MPa -
Yield strength Rp0.2 23.0 °C Yield strength Rp0.2 of 1079 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us