JIS G4318 Grade SUS305
Equivalent material: GOST 06Х18Н11, DIN X5CrNi1812, NF Z8CN18-12, NF X8CN18-12, NF Z5CN18-11FF, BS 305S17, BS 305S19, UNI X8CrNi1910, UNI X7CrNi1810, ÖNORM X5CrNi1812KKW, EN X4CrNi18-12, UNE X8CrNi1812, AMS 5514, AMS 5685, AMS 5686, ASME 305, ASTM 305, ASTM B8P, ASTM B8PA, ASTM 8P, ASTM TP305, ASTM MT305, ASTM 8PA, JIS SUS305J1, AISI 305, SAE 305, ASTM 308, AISI 308, DIN 1.4303, DIN X5CrNi18-12, DIN X4CrNi18-12, AFNOR Z1CN18-12, AFNOR Z5CN18-11FF, SAE 308, JIS SUSY308, EN 1.4303, GOST 06Ch18N11, GOST 06X18H11, GB 1Cr18Ni12, ASTM ER308, UNS S30500, UNS S30880
JIS G4318 Grade SUS305 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4318 Grade SUS305 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4318 Grade SUS305 magnetic
| Property |
Value |
| Carbon |
Carbon of 0.12 % |
| Chromium |
Chromium of 17 - 19 % |
| Iron |
Iron of 64.8 - 72.5 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 10.5 - 13 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
JIS G4318 Grade SUS305 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4318 Grade SUS305 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |