JIS G4306 Grade SUS420J2 hot-rolled and annealed

Equivalent material: DIN 1.4028, DIN X30Cr13, AFNOR Z33C13, BS 420S45, AISI 420F, SAE 420F, JIS SUS420J2FB, JIS SUS420J2TKA, EN X30Cr13, EN 1.4028, ISO 30Cr13, GOST 30Ch13, GB 3Cr13, ASTM 420F, UNS S42000

JIS G4306 Grade SUS420J2 hot-rolled and annealed general

Property Temperature Value Comment
Density 23.0 °C Density of 7.6 - 7.7 g/cm³ Typical for Martensitic Stainless Steel

JIS G4306 Grade SUS420J2 hot-rolled and annealed thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K Typical for Martensitic Stainless Steel
Melting point - Melting point of 1370 - 1530 °C Typical for Martensitic Stainless Steel
Specific heat capacity 23.0 °C Specific heat capacity of 460 J/(kg·K) Typical for Martensitic Stainless Steel
Thermal conductivity 23.0 °C Thermal conductivity of 14 - 31 W/(m·K) Typical for Martensitic Stainless Steel

JIS G4306 Grade SUS420J2 hot-rolled and annealed magnetic

Property - -
Processing history

JIS G4306 Grade SUS420J2 hot-rolled and annealed electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 6E-7 Ω·m Typical for Martensitic Stainless Steel

JIS G4306 Grade SUS420J2 hot-rolled and annealed mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 220 GPa Typical for Martensitic Stainless Steel
Elongation 23.0 °C Elongation of 18 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.3 [-] Typical for Martensitic Stainless Steel
Shear modulus 23.0 °C Shear modulus of 77 GPa Typical for Martensitic Stainless Steel
Tensile strength 23.0 °C Tensile strength of 539 MPa -
Yield strength 23.0 °C Yield strength of 226 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us

Message