JIS G4305 Grade SUS316N solution treated

Equivalent material: BS 316S65, BS 316S67, ASME 316N, ASTM TP316N, ASTM 316N, ASTM CR316N, ASTM WP316N, ASTM 18Cr, ASTM F316N, ASTM 8MN, ASTM FP316N, ASTM B8MN, ASTM B8MNA, ASTM 8MNA, AISI 316N, SAE 316N, UNS S31651, ASTM S31651, ASTM Grade 8MN

JIS G4305 Grade SUS316N solution treated general

Property Temperature Value Comment
Density 23.0 °C Density of 7.9 - 8.2 g/cm³ Typical for Austenitic Stainless Steel

JIS G4305 Grade SUS316N solution treated thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K Typical for Austenitic Stainless Steel
Melting point - Melting point of 1230 - 1480 °C Typical for Austenitic Stainless Steel
Specific heat capacity 23.0 °C Specific heat capacity of 440 J/(kg·K) Typical for Austenitic Stainless Steel
Thermal conductivity 23.0 °C Thermal conductivity of 11 - 21 W/(m·K) Typical for Austenitic Stainless Steel

JIS G4305 Grade SUS316N solution treated magnetic

Property - -
Processing history

JIS G4305 Grade SUS316N solution treated electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 8.5E-7 Ω·m Typical for Austenitic Stainless Steel

JIS G4305 Grade SUS316N solution treated mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 195 GPa Typical for Austenitic Stainless Steel
Elongation A5 23.0 °C Elongation A5 of 40 % -
Hardness, Brinell 23.0 °C Hardness, Brinell of 217 [-] -
Hardness, Rockwell B 23.0 °C Hardness, Rockwell B of 95 [-] -
Hardness, Vickers 23.0 °C Hardness, Vickers of 220 [-] -
Poisson's ratio 23.0 °C Poisson's ratio of 0.3 [-] Typical for Austenitic Stainless Steel
Shear modulus 23.0 °C Shear modulus of 77 GPa Typical for Austenitic Stainless Steel
Tensile strength 23.0 °C Tensile strength of 550 MPa -
Yield strength Rp0.2 23.0 °C Yield strength Rp0.2 of 275 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us

Message