JIS G4304 Grade SUS631
Equivalent material: GB/T 0Cr17Ni7Al, GB 0Cr17Ni7Al, GOST 09Х17Н7Ю1, GOST 09H17N7Yu1, DIN X7CrNiAl177, NF Z8CNA17-07, NF Z9CNA17-07, BS 301S81, EN X7CrNiAl17-7, SIS 2388, AMS 5528, AMS 5529, AMS 5568, AMS 5644, AMS 5673, AMS 5678, ASME 631, ASTM 631, ASTM 62, MIL 17-7PH, MIL S-25043, JIS SUS631J1, AISI 631, SAE 17-7PH, SAE 631, UNS S17700, DIN 1.4568, DIN X 7 CrNiAl 17 7, AFNOR Z9CNA17-07, AISI 631 (17-7PH), SAE 631 (17-7PH), JIS SUS631-CSP, EN 1.4568
JIS G4304 Grade SUS631 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
JIS G4304 Grade SUS631 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 3 - 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 192 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 92 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 35 - 40 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 - 392 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 1030 - 1230 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 380 - 1030 MPa |
- |