JIS G4303 Grade SUS630
Equivalent material: GB/T 0Cr17Ni4Cu4Nb, AS 630, NF Z6CNU17-04, NF Z7CNU17-04, NF Z7CNU15-05, EN X5CrNiCuNb16-4, AMS 5604, AMS 5622, AMS 5643, AMS 7474, ASME 630, ASTM CB7Cu-1, ASTM 630, MIL C-24111, MIL S-81591, JIS SCS24, AISI 630, SAE 17-4PH, NF Z7CNU16-04, DIN 1.4542, DIN X5CrNiCuNb16-4, DIN X5CrNiCuNb17-4, AFNOR Z7CNU15-05, AFNOR Z7CNU17-04, BS X5CrNiCuNb16-4, AISI 17-4PH, AISI 630 (17-4PH), SAE 630, SAE 630 (17-4PH), JIS SUSF630, EN 1.4542, ISO X5CrNiCuNb16-4, ISO PP20I, ISO 4542-174-00-I, GB 05Cr17Ni4Cu4Nb, ASTM 17-4PH, ASTM S17400, ASTM Grade F Class 1, UNS S17400
JIS G4303 Grade SUS630 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
JIS G4303 Grade SUS630 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 10 - 16 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 277 - 375 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 28 - 40 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 40 - 50 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 930 - 1310 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 725 - 1175 MPa |
- |