JIS G4109 Grade SCMV5
Equivalent material: DIN 1.7767, DIN 12CrMoV12-10, DIN 20CrMoVTiB4-10, BS 12CrMoV12-10, JIS SCMQV5, JIS SFVCMF3V, JIS SCMQ5V, EN 12CrMoV12-10, EN 20CrMoVTiB4-10, EN 1.7767, ISO 12CrMoV12-10, ISO 13CrMoV12-10, ISO 14CrMoV9-10, ASTM Type D Class 1, ASTM Type E Class 4, ASTM Grade 3V, ASTM Grade F3VCb
JIS G4109 Grade SCMV5 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
JIS G4109 Grade SCMV5 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
JIS G4109 Grade SCMV5 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 410 - 690 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 205 - 315 MPa |
- |