JIS G4109 Grade SCMV2
Equivalent material: DIN 1.7335, DIN 13CrMo4-4, DIN 13CrMo4-5, AFNOR 15CD3.5, AFNOR 15CD4.5, BS 1501-620-Gr27, BS 13CrMo4-5, UNI 14CrMo45, UNE 14CrMo45, JIS SPVAF12, JIS STPA22, JIS STBA22, JIS STFA22, JIS STBA20, JIS SFVAF12, EN 13CrMo4-5, EN 1.7335, ISO 13CrMo4-5, ISO 14CrMo4-5+NT1, ISO 14CrMo4-5+NT2, ASTM Grade T2, UNS K11562
JIS G4109 Grade SCMV2 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
JIS G4109 Grade SCMV2 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
JIS G4109 Grade SCMV2 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 18 - 22 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 380 - 590 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 225 - 275 MPa |
- |