JIS G4051 Grade S33C
Equivalent material: GOST 30H, GOST 30Г, GOST 30G, ASTM 1033, AISI 1033, SAE 1033, GB/T 30Mn, GB/T 30Mn, GB/T ML30Mn, GB 35, GB ZG270-500(ZG35), GOST 35, EN C35E, DIN Ck35, NF XC32, NF XC, NF XC38H2, NF XC35, NF XC38H1, ÖNORM C35SW, ÖNORM Ck35S, UNE C35K, ASTM 1034, JIS S38C, AISI 1034, DIN 1.1170, DIN 28Mn6, DIN ETG 25, AFNOR 28Mn6, AFNOR 20M5, BS 26Mn6, BS En14A, BS En14B, BS 150M19, AISI 1330H, AISI 1527, AISI 1330, AISI 1524, SAE 1330H, SAE 1527, SAE 1330, SAE 1524, JIS SCMn1A, JIS SCMn1B, JIS SCMn1, EN 28Mn6, EN 1.1170, ISO 28Mn6, GOST 30G2, GB 30Mn2, GB A00302, GB/T 30Mn2, GB/T A00302, UNS H13300, UNS G13300, IS 20Mn2, IS 20C15
JIS G4051 Grade S33C general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Manganese Steel |
JIS G4051 Grade S33C thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.33E-5 1/K |
Typical for Manganese Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Manganese Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 510 - 553 J/(kg·K) |
Typical for Manganese Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 16 W/(m·K) |
Typical for Manganese Steel |
JIS G4051 Grade S33C electrical
| Property |
Value |
| Carbon |
Carbon of 0.3 - 0.36 % |
| Iron |
Iron of 98.32 - 98.95 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.035 % |
JIS G4051 Grade S33C mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Manganese Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Manganese Steel |