JIS G3545 Grade SWCHB420
Equivalent material: DIN 19MnB4, NF 25B3, NF 21B3, BS 170H20, EN 19MnB4, UNE 20MnB4DF, ASTM 15B21H, AISI 15B21H, SAE 15B21H, DIN 1.5523, AFNOR 19MnB4, UNI 19MnB4, JIS SWRCHB420, EN 1.5523, GOST 20G2R, GB ML20MnB, ASTM Grade 15B21RH, ASTM 15B21RH, UNS H15211
JIS G3545 Grade SWCHB420 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3545 Grade SWCHB420 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3545 Grade SWCHB420 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3545 Grade SWCHB420 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3545 Grade SWCHB420 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 92 - 100 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 - 55 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 600 - 750 MPa |
- |