JIS G3214 Grade SUSF630
Equivalent material: DIN 1.4542, DIN X5CrNiCuNb16-4, DIN X5CrNiCuNb17-4, AFNOR Z7CNU15-05, AFNOR Z7CNU17-04, BS X5CrNiCuNb16-4, AISI 630, AISI 17-4PH, AISI 630 (17-4PH), SAE 630, SAE 17-4PH, SAE 630 (17-4PH), JIS SUS630, JIS SCS24, EN X5CrNiCuNb16-4, EN 1.4542, ISO X5CrNiCuNb16-4, ISO PP20I, ISO 4542-174-00-I, GB 05Cr17Ni4Cu4Nb, ASTM 17-4PH, ASTM 630, ASTM CB7Cu-1, ASTM S17400, ASTM Grade F Class 1, UNS S17400
JIS G3214 Grade SUSF630 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
JIS G3214 Grade SUSF630 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 12 - 15 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 277 - 311 [-] |
- |
| Impact strength, Charpy notched |
20.0 °C |
Impact strength, Charpy notched of 27 - 41 kJ/m² |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 - 50 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 930 - 1000 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 725 - 860 MPa |
- |