JIS G3203 Grade SFVAF5D
Equivalent material: DIN 1.7362, DIN 12 CrMo 19 5, DIN X11CrMo5, DIN 12CrMo19-5, DIN X12CrMo5, AFNOR Z10CD5.05, BS 3606-625, BS X11CrMo5, BS X12CrMo5, UNI 16CrMo205, JIS SFVAF5A, JIS SFVAF5B, JIS STPA25, JIS STBA25, JIS STFA25, JIS SCMV6, JIS SFVAF5C, JIS SNB5, EN X12CrMo5, EN X11CrMo5, EN 1.7362, ISO X12CrMo5, ISO X12CrMo5-1, ISO F37, ASTM Grade T5, ASTM Grade B5, ASTM Grade P5, DIN 1.7366, DIN X16CrMo5-1, EN X16CrMo5-1, EN 1.7366
JIS G3203 Grade SFVAF5D general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
JIS G3203 Grade SFVAF5D thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
JIS G3203 Grade SFVAF5D mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 35 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 620 - 780 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 450 MPa |
- |