EN 10292 Grade HX260YD hot rolled or cold rolled, hot dip coated,+Z, +ZF, +ZA, +AZ, +AS

EN 10292 Grade HX260YD hot rolled or cold rolled, hot dip coated,+Z, +ZF, +ZA, +AZ, +AS introduction

The steel HX260YD (X=roll condition, Y=interstitial free, D=hot-dip coatable) is producible with the following coatings:
- HX260YD+Z (plating Zn) with coating weights (double-sided) of 100, 140, 200, 225 and 275 g/m² (100 g approximate 7,1 µm per side)
- HX260YD+ZF (plating Zn-Fe) with coating weights (double-sided) of 100 and 120 g/m² (100 g approximate 7,1 µm per side)
- HX260YD+ZA (plating Zn-Al) with coating weights (double-sided) of 095, 130, 185, 200 and 255 g/m² (95 g approximate 7,2 µm per side)
- HX260YD+AZ (plating Al-Zn) with coating weights (double-sided) of 100, 150 and 185 g/m² (100 g approximate 13,3 µm per side)
- HX260YD+AS (plating Al-Si) with coating weights (double-sided) of 060 and 080 g/m² (100 g approximate 17 µm per side)
The hot dip galvanizing refined flat products are available by arrangement on ordering with different coating weights (also per side).
Following surface protection types can be delivered: chemical passivated, oiled, chemical passivated and oiled, sealed, phosphated, phosphated and oiled.
Mechanical properties are warranted for a period of 3 months for Bake-hardening steels and for a period of 6 months after provision of the products for all other sorts. The same terms are valid for freedom from stretcher strains (surface type B and C).
It is suitable for usual welding methods. For higher coating weights on welding are where approppriate necessary special measures.
Furthermore suitability for joining by sticking as well as for application of organic coatings.
Application:
household appliances industry, construction trade, electrical industry, furniture industry, car industry.,The steel HX260YD (X=roll condition, Y=interstitial free, D=hot-dip coatable) is deliverable with the following coatings:
- HX260YD+Z (plating Zn) with coating weights (double-sided) of 100, 140, 200, 225 and 275 g/m² (100 g approximate 7,1 µm per side)
- HX260YD+ZF (plating Zn-Fe) with coating weights (double-sided) of 100 and 120 g/m² (100 g approximate 7,1 µm per side)
- HX260YD+ZA (plating Zn-Al) with coating weights (double-sided) of 095, 130, 185, 200 and 255 g/m² (95 g approximate 7,2 µm per side)
- HX260YD+AZ (plating Al-Zn) with coating weights (double-sided) of 100, 150 and 185 g/m² (100 g approximate 13,3 µm per side)
- HX260YD+AS (plating Al-Si) with coating weights (double-sided) of 060 and 080 g/m² (100 g approximate 17 µm per side)
The hot dip galvanizing refined flat products are available by arrangement on ordering with different coating weights (also per side).
Following surface protection types can be delivered: chemical passivated, oiled, chemical passivated and oiled, sealed, phosphated, phosphated and oiled.
Mechanical properties are warranted for a period of 6 months after provision. The same time is valid for freedom from stretcher strains (surface type B and C).
It is suitable for usual welding methods. For higher coating weights on welding are where approppriate necessary special measures.
Furthermore suitability for joining by sticking as well as for application of organic coatings.
Application:
household appliances industry, construction trade, electrical industry, furniture industry, car industry.

EN 10292 Grade HX260YD hot rolled or cold rolled, hot dip coated,+Z, +ZF, +ZA, +AZ, +AS general

Property Temperature Value
Elongation A80, transverse 20.0 °C Elongation A80, transverse of 30 %
Tensile strength, transverse 20.0 °C Tensile strength, transverse of 380 - 440 MPa
Yield strength Rp0.2, transverse 20.0 °C Yield strength Rp0.2, transverse of 260 - 320 MPa

EN 10292 Grade HX260YD hot rolled or cold rolled, hot dip coated,+Z, +ZF, +ZA, +AZ, +AS mechanical

Property Value
Aluminium Aluminium of 0.02 %
Carbon Carbon of 0.01 %
Manganese Manganese of 1.6 %
Niobium Niobium of 0.09 %
Phosphorus Phosphorus of 0.1 %
Silicon Silicon of 0.1 - 0.25 %
Sulfur Sulfur of 0.025 %
Titanium Titanium of 0.12 %

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us

Message