EN 10216-4 Grade X10Ni9 normalized, normalized and tempered (+N+NT)
EN 10216-4 Grade X10Ni9 normalized, normalized and tempered (+N+NT) introduction
Seamless steel tube for pressure purposes with specified low temperature properties.,Tubes made from cryogenic alloyed high-grade steel X10Ni9 are predominantly used in apparatus, tank, line construction as well as in general machine and equipment engineering.
Weldability is available.
EN 10216-4 Grade X10Ni9 normalized, normalized and tempered (+N+NT) general
| Property |
Temperature |
Value |
| Elongation |
20.0 °C |
Elongation of 20 % |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 18 % |
| Tensile strength |
20.0 °C |
Tensile strength of 690 - 840 MPa |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 690 - 840 MPa |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 510 MPa |
| - |
100.0 °C |
Yield strength Rp0.2 of 370 MPa |
| - |
200.0 °C |
Yield strength Rp0.2 of 335 MPa |
| - |
250.0 °C |
Yield strength Rp0.2 of 315 MPa |
| - |
300.0 °C |
Yield strength Rp0.2 of 300 MPa |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 510 MPa |
EN 10216-4 Grade X10Ni9 normalized, normalized and tempered (+N+NT) mechanical
| Property |
Value |
| Carbon |
Carbon of 0.13 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.3 - 0.8 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 8.5 - 9.5 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.005 - 0.01 % |
| Vanadium |
Vanadium of 0.05 % |