EN 10209 Grade DC03ED cold rolled, skin passed

EN 10209 Grade DC03ED cold rolled, skin passed introduction

Cold rolled low carbon steel for flat products for vitreous enamelling (direct enamelling, as well as for special applications of conventional two coat enamelling for better sag resistance).
Application: domestic appliances (cooking, laundry), sanitary ware (bathtubs, shower trays, sinks), architectural panels (interior and exterior), signage,The soft unalloyed steel DCO1ED, mat. No. 1.0399, is a cold formable steel and suitable for direct enameling as well as for special conventional applications of two-coat enameling, especially if there should be preferably enameled non deforming. In this case are necessary special measures in order to improve enamel`s adhesion. Mechanical specific values and freedom of stretcher strains are warranted for 6 months.
Application: simple reforming parts
pots, pans, covering caps for gas kitchen stoves, baking sheets, simple shower bases etc.
Welding: DC01ED is weldable acc. to the fusion welding methods:
MAG (metal active gas/plasma welding
arc hand welding
laser welding
gas welding
resistance welding (spot, roll seam, buckle welding)

Equivalent material: DIN ED3, JIS SPP, ASTM I, DIN 1.0399, DIN FeD 3, DIN CR1, DIN CR3, DIN DC03ED, AFNOR DC03ED, BS DC03ED, BS CR1, BS CR3, EN 1.0399

EN 10209 Grade DC03ED cold rolled, skin passed general

Property Temperature Value Comment
Density 20.0 °C Density of 7.8 - 7.9 g/cm³ Typical for Low Carbon Steel

EN 10209 Grade DC03ED cold rolled, skin passed thermal

Property Temperature Value Comment
Coefficient of thermal expansion 20.0 °C Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K Typical for Low Carbon Steel
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel

EN 10209 Grade DC03ED cold rolled, skin passed magnetic

Property Value
Carbon Carbon of 4E-3 %
Manganese Manganese of 0.4 %
Phosphorus Phosphorus of 0.04 %
Sulfur Sulfur of 0.05 %

EN 10209 Grade DC03ED cold rolled, skin passed electrical

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

EN 10209 Grade DC03ED cold rolled, skin passed mechanical

Property Temperature Value Comment
Elastic modulus 20.0 °C Elastic modulus of 200 - 215 GPa Typical for Low Carbon Steel
Elongation A80 20.0 °C Elongation A80 of 34 % -
Elongation A80, transverse 20.0 °C Elongation A80, transverse of 30 - 34 % -
Poisson's ratio 20.0 °C Poisson's ratio of 0.29 [-] Typical for Low Carbon Steel
Tensile strength 20.0 °C Tensile strength of 270 - 370 MPa -
Tensile strength, transverse 20.0 °C Tensile strength, transverse of 270 - 370 MPa -
Yield strength 20.0 °C Yield strength of 140 - 240 MPa -
Yield strength, transverse 20.0 °C Yield strength, transverse of 140 - 280 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us

Message