EN 10084 Grade 17CrNi6-6 quenched (+Q)
EN 10084 Grade 17CrNi6-6 quenched (+Q) introduction
The case-hardening steel is mainly used for gear parts, but also in the mechanical engineering.
Equivalent material: GB 17Cr2Ni2H, EN 1.5918, IS 14CrNi6(-S), ISO 17CrNi6-6, DIN 1.5918
EN 10084 Grade 17CrNi6-6 quenched (+Q) general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
EN 10084 Grade 17CrNi6-6 quenched (+Q) thermal
| Property | Value |
|---|---|
| Carbon | Carbon of 0.14 - 0.2 % |
| Chromium | Chromium of 1.4 - 1.7 % |
| Copper | Copper of 0.4 % |
| Manganese | Manganese of 0.5 - 0.9 % |
| Nickel | Nickel of 1.4 - 1.7 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.15 - 0.4 % |
| Sulfur | Sulfur of 0.035 % |
EN 10084 Grade 17CrNi6-6 quenched (+Q) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Tensile strength | 20.0 °C | Tensile strength of 800 - 1200 MPa | - |