EN 10084 Grade 16NiCrS4 quenched (+Q)
EN 10084 Grade 16NiCrS4 quenched (+Q) introduction
The case-hardening steel is mainly used for gear parts, but also in the mechanical engineering.
Equivalent material: EN 1.5715, IS 16Ni3Cr2(-S), ISO 16NiCrS4, DIN 1.5715, DIN 16NiCrS4
EN 10084 Grade 16NiCrS4 quenched (+Q) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
EN 10084 Grade 16NiCrS4 quenched (+Q) thermal
| Property |
Value |
| Carbon |
Carbon of 0.13 - 0.19 % |
| Chromium |
Chromium of 0.6 - 1 % |
| Copper |
Copper of 0.4 % |
| Manganese |
Manganese of 0.7 - 1 % |
| Nickel |
Nickel of 0.8 - 1.1 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.02 - 0.04 % |
EN 10084 Grade 16NiCrS4 quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 800 - 1000 MPa |
- |