EN 10083-2 Grade C60R soft annealed (+A)
EN 10083-2 Grade C60R soft annealed (+A) introduction
Steel C60R is suitable for high loaded parts in vehicle manufacturing, engine and machine engineering requiring improved workability while maintaining constant strength properties (e.g. gear wheels, pinions, shafts).
As a bright steel product it is used in the form of bars, bright, straight, in different conditions (see DIN EN 10277).
Equivalent material: IS 60C8, ISO C60R, JIS S58C, KS SM58C, GOST 60, ASTM A29 Grade 1060, ASTM A29 Grade 1064, ASTM A510 Grade 1060, ASTM A510 Grade 1064, ASTM A576 Grade 1060, UNS G10600, UNS G10640, SAE 1060, DIN Cm60, EN 1.1223, ASTM A827 Grade 1060, ASTM A830 Grade 1060, DIN 1.1223, DIN Cm 60, DIN C60R, AFNOR C60R, BS C60R, AISI 1060, ISO C60M2
EN 10083-2 Grade C60R soft annealed (+A) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10083-2 Grade C60R soft annealed (+A) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 51 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 49.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 47.8 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 44.8 W/(m·K) |
- |
EN 10083-2 Grade C60R soft annealed (+A) magnetic
| Property |
Value |
| Carbon |
Carbon of 0.57 - 0.65 % |
| Chromium |
Chromium of 0.4 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.1 - 0.4 % |
| Sulfur |
Sulfur of 0.02 - 0.04 % |
EN 10083-2 Grade C60R soft annealed (+A) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.3E-7 Ω·m |
EN 10083-2 Grade C60R soft annealed (+A) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |