DIN 17100 St 37-2 Hot Rolled
Equivalent material: DIN 1.0037, DIN S235JR
DIN 17100 St 37-2 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
DIN 17100 St 37-2 Hot Rolled thermal
| Property |
Temperature |
Value |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 461 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 54 W/(m·K) |
DIN 17100 St 37-2 Hot Rolled magnetic
| Property |
Value |
| Carbon |
Carbon of 0.2 % |
| Iron |
Balance |
| Manganese |
Manganese of 1.25 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.12 % |
| Sulfur |
Sulfur of 0.035 % |
DIN 17100 St 37-2 Hot Rolled electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.5E-7 Ω·m |
DIN 17100 St 37-2 Hot Rolled mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 210 GPa |
| Elongation |
23.0 °C |
Elongation of 17 % |
| Tensile strength |
23.0 °C |
Tensile strength of 340 - 510 MPa |
| Yield strength |
23.0 °C |
Yield strength of 225 MPa |