ASTM A982 Grade D Class 1 Quenched and Tempered; Stress-Relieved
ASTM A982 Grade D Class 1 Quenched and Tempered; Stress-Relieved general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A982 Grade D Class 1 Quenched and Tempered; Stress-Relieved thermal
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.025 % |
| Carbon | Carbon of 0.2 - 0.25 % |
| Chromium | Chromium of 11 - 12.5 % |
| Cobalt | Cobalt of 0.2 % |
| Copper | Copper of 0.15 % |
| Manganese | Manganese of 0.5 - 1 % |
| Molybdenum | Molybdenum of 0.9 - 1.25 % |
| Nickel | Nickel of 0.5 - 1 % |
| Niobium | Niobium of 0.05 % |
| Phosphorus | Phosphorus of 0.02 % |
| Silicon | Silicon of 0.2 - 0.5 % |
| Sulfur | Sulfur of 0.01 % |
| Tin | Tin of 0.02 % |
| Titanium | Titanium of 0.03 % |
| Tungsten | Tungsten of 0.9 - 1.25 % |
| Vanadium | Vanadium of 0.2 - 0.3 % |
ASTM A982 Grade D Class 1 Quenched and Tempered; Stress-Relieved mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Charpy impact energy | 23.0 °C | Charpy impact energy of 11 J | - |
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 13 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 331 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Reduction of area | 23.0 °C | Reduction of area of 30 % | - |
| Tensile strength | 23.0 °C | Tensile strength of 965 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 620 MPa | - |