ASTM A813 Grade TP304N Heat-Treated

Equivalent material: DIN 1.4315, BS 304S65, AISI 304N, SAE 304N, JIS SUS304N1, JIS SCS13A, JIS SUSF304N, EN X5CrNiN19-9, EN 1.4315, UNS S30451, ASTM 304N, ASTM 304N

ASTM A813 Grade TP304N Heat-Treated general

Property Temperature Value Comment
Density 23.0 °C Density of 7.6 - 7.8 g/cm³ Typical for Ferritic Stainless Steel

ASTM A813 Grade TP304N Heat-Treated thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K Typical for Ferritic Stainless Steel
Melting point - Melting point of 1425 - 1530 °C Typical for Ferritic Stainless Steel
Specific heat capacity 23.0 °C Specific heat capacity of 420 - 586 J/(kg·K) Typical for Ferritic Stainless Steel
Thermal conductivity 23.0 °C Thermal conductivity of 11 - 22 W/(m·K) Typical for Ferritic Stainless Steel

ASTM A813 Grade TP304N Heat-Treated magnetic

Property Value
Carbon Carbon of 0.08 %
Chromium Chromium of 18 - 20 %
Manganese Manganese of 2 %
Nickel Nickel of 8 - 11 %
Nitrogen Nitrogen of 0.1 - 0.16 %
Phosphorus Phosphorus of 0.05 %
Silicon Silicon of 1 %
Sulfur Sulfur of 0.03 %

ASTM A813 Grade TP304N Heat-Treated electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 6E-7 - 7.5E-7 Ω·m Typical for Ferritic Stainless Steel

ASTM A813 Grade TP304N Heat-Treated mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 220 GPa Typical for Ferritic Stainless Steel
Poisson's ratio 23.0 °C Poisson's ratio of 0.3 [-] Typical for Ferritic Stainless Steel
Shear modulus 23.0 °C Shear modulus of 77 GPa Typical for Ferritic Stainless Steel
Tensile strength 23.0 °C Tensile strength of 550 MPa -
Yield strength 23.0 °C Yield strength of 240 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us

Message