ASTM A738 Grade C Heat-Treated
ASTM A738 Grade C Heat-Treated general
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Charpy impact energy | Charpy impact energy of 27 J | Heat-Treated | ASTM A738 | Plate |
| Tensile strength | Tensile strength of 485 - 620 MPa | Heat-Treated | ASTM A738 | Plate |
| - | Tensile strength of 515 - 655 MPa | Heat-Treated | ASTM A738 | Plate |
| - | Tensile strength of 550 - 690 MPa | Heat-Treated | ASTM A738 | Plate |
| Yield strength | Yield strength of 315 MPa | Heat-Treated | ASTM A738 | Plate |
| - | Yield strength of 380 MPa | Heat-Treated | ASTM A738 | Plate |
| - | Yield strength of 415 MPa | Heat-Treated | ASTM A738 | Plate |
ASTM A738 Grade C Heat-Treated thermal
| Property | - | - |
|---|---|---|
| Supplier Disclaimer |
ASTM A738 Grade C Heat-Treated mechanical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Carbon | Carbon of 0.2 % | Heat-Treated | ASTM A738 | Plate |
| Chromium | Chromium of 0.25 % | Heat-Treated | ASTM A738 | Plate |
| Copper | Copper of 0.35 % | Heat-Treated | ASTM A738 | Plate |
| Manganese | Manganese of 1.5 % | Heat-Treated | ASTM A738 | Plate |
| Molybdenum | Molybdenum of 0.08 % | Heat-Treated | ASTM A738 | Plate |
| Nickel | Nickel of 0.5 % | Heat-Treated | ASTM A738 | Plate |
| Phosphorus | Phosphorus of 0.025 % | Heat-Treated | ASTM A738 | Plate |
| Silicon | Silicon of 0.15 - 0.5 % | Heat-Treated | ASTM A738 | Plate |
| Sulfur | Sulfur of 0.025 % | Heat-Treated | ASTM A738 | Plate |
| Vanadium | Vanadium of 0.05 % | Heat-Treated | ASTM A738 | Plate |