ASTM A705 Grade XM-16 Age-Hardening H1000

Equivalent material: DIN 1.4543, DIN X3CrNiCuTi12-9, DIN X3CrNiCuTiNb12-9, AISI S45500, AISI XM-16, SAE S45500, SAE XM-16, EN 1.4543, UNS S45500

ASTM A705 Grade XM-16 Age-Hardening H1000 general

Property Temperature Value Comment
Density 23.0 °C Density of 7.8 g/cm³ Typical for Steel

ASTM A705 Grade XM-16 Age-Hardening H1000 thermal

Property Value
Carbon Carbon of 0.03 %
Chromium Chromium of 11 - 12.5 %
Copper Copper of 1.5 - 2.5 %
Manganese Manganese of 0.5 %
Molybdenum Molybdenum of 0.5 %
Nickel Nickel of 7.5 - 9.5 %
Phosphorus Phosphorus of 0.02 %
Silicon Silicon of 0.5 %
Sulfur Sulfur of 0.015 %
Titanium Titanium of 0.9 - 1.4 %

ASTM A705 Grade XM-16 Age-Hardening H1000 mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 190 - 210 GPa Typical for Steel
Elongation A50 23.0 °C Elongation A50 of 10 % -
Hardness, Brinell 23.0 °C Hardness, Brinell of 363 [-] -
Hardness, Rockwell C 23.0 °C Hardness, Rockwell C of 40 [-] -
Poisson's ratio 23.0 °C Poisson's ratio of 0.3 [-] Typical for Steel
Reduction of area 23.0 °C Reduction of area of 40 % -
Tensile strength 23.0 °C Tensile strength of 1410 MPa -
Yield strength 23.0 °C Yield strength of 1280 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us

Message