ASTM A705 Grade S45503 Age-Hardening H950
Equivalent material: UNS S45503
ASTM A705 Grade S45503 Age-Hardening H950 general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A705 Grade S45503 Age-Hardening H950 thermal
| Property | Value |
|---|---|
| Carbon | Carbon of 0.01 % |
| Chromium | Chromium of 11 - 12.5 % |
| Copper | Copper of 1.5 - 2.5 % |
| Manganese | Manganese of 0.5 % |
| Molybdenum | Molybdenum of 0.5 % |
| Nickel | Nickel of 7.5 - 9.5 % |
| Phosphorus | Phosphorus of 0.01 % |
| Silicon | Silicon of 0.2 % |
| Sulfur | Sulfur of 0.01 % |
| Titanium | Titanium of 1 - 1.35 % |
ASTM A705 Grade S45503 Age-Hardening H950 mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 5 - 10 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 415 [-] | - |
| Hardness, Rockwell C | 23.0 °C | Hardness, Rockwell C of 44 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Reduction of area | 23.0 °C | Reduction of area of 20 - 40 % | - |
| Tensile strength | 23.0 °C | Tensile strength of 1520 MPa | - |
| Yield strength | 23.0 °C | Yield strength of 1410 MPa | - |