ASTM A705 Grade 635 Age-Hardening H1050
Equivalent material: UNS S17600
ASTM A705 Grade 635 Age-Hardening H1050 general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A705 Grade 635 Age-Hardening H1050 thermal
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.4 % |
| Carbon | Carbon of 0.08 % |
| Chromium | Chromium of 16 - 17.5 % |
| Manganese | Manganese of 1 % |
| Nickel | Nickel of 6 - 7.5 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.03 % |
| Titanium | Titanium of 0.4 - 1.2 % |
ASTM A705 Grade 635 Age-Hardening H1050 mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 10 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 331 [-] | - |
| Hardness, Rockwell C | 23.0 °C | Hardness, Rockwell C of 35 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Reduction of area | 23.0 °C | Reduction of area of 40 % | - |
| Tensile strength | 23.0 °C | Tensile strength of 1170 MPa | - |
| Yield strength | 23.0 °C | Yield strength of 1035 MPa | - |