ASTM A693 Grade 632 Precipitation hardened at 760 °C + 15 °C + 566 °C

Equivalent material: UNS S15700

ASTM A693 Grade 632 Precipitation hardened at 760 °C + 15 °C + 566 °C general

Property Temperature Value Comment
Density 23.0 °C Density of 7.8 g/cm³ Typical for Steel

ASTM A693 Grade 632 Precipitation hardened at 760 °C + 15 °C + 566 °C thermal

Property Value
Aluminium Aluminium of 0.75 - 1.5 %
Carbon Carbon of 0.09 %
Chromium Chromium of 14 - 16 %
Manganese Manganese of 1 %
Molybdenum Molybdenum of 2 - 3 %
Nickel Nickel of 6.5 - 7.7 %
Phosphorus Phosphorus of 0.04 %
Silicon Silicon of 1 %
Sulfur Sulfur of 0.03 %

ASTM A693 Grade 632 Precipitation hardened at 760 °C + 15 °C + 566 °C mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 190 - 210 GPa Typical for Steel
Elongation A50 23.0 °C Elongation A50 of 2 - 5 % -
Hardness, Brinell 23.0 °C Hardness, Brinell of 375 [-] -
Hardness, Rockwell C 23.0 °C Hardness, Rockwell C of 40 [-] -
Poisson's ratio 23.0 °C Poisson's ratio of 0.3 [-] Typical for Steel
Reduction of area 23.0 °C Reduction of area of 20 % -
Tensile strength 23.0 °C Tensile strength of 1310 MPa -
Yield strength 23.0 °C Yield strength of 1170 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us

Message