ASTM A581 Grade S18235 Cold Worked
Equivalent material: DIN 1.4523, EN X2CrMoTiS18-2, EN 1.4523, UNS S18235
ASTM A581 Grade S18235 Cold Worked general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.6 - 7.8 g/cm³ | Typical for Ferritic Stainless Steel |
ASTM A581 Grade S18235 Cold Worked thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K | Typical for Ferritic Stainless Steel |
| Melting point | - | Melting point of 1425 - 1530 °C | Typical for Ferritic Stainless Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 420 - 586 J/(kg·K) | Typical for Ferritic Stainless Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 11 - 22 W/(m·K) | Typical for Ferritic Stainless Steel |
ASTM A581 Grade S18235 Cold Worked magnetic
| Property | Value |
|---|---|
| Carbon | Carbon of 0.025 % |
| Chromium | Chromium of 17.5 - 18.5 % |
| Manganese | Manganese of 0.5 % |
| Nickel | Nickel of 1 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.15 - 0.35 % |
ASTM A581 Grade S18235 Cold Worked electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 6E-7 - 7.5E-7 Ω·m | Typical for Ferritic Stainless Steel |
ASTM A581 Grade S18235 Cold Worked mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 220 GPa | Typical for Ferritic Stainless Steel |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Ferritic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Ferritic Stainless Steel |
| Tensile strength | 23.0 °C | Tensile strength of 415 - 620 MPa | - |