ASTM A534 Grade 4320H
Equivalent material: DIN 1.5919, DIN 15CrNi6, AFNOR 16NC6, AISI 4320H, AISI 4320, AISI 4617, SAE 4320H, SAE 4320, SAE 4617, JIS SNCM415, JIS SNCM415M, EN 1.5919, ASTM 4320, UNS H43200, UNS G43200, UNS G46170
ASTM A534 Grade 4320H general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Nickel Chromium Molybdenum Steel |
ASTM A534 Grade 4320H thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.3E-5 1/K |
Typical for Nickel Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Nickel Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 670 J/(kg·K) |
Typical for Nickel Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 34 - 54 W/(m·K) |
Typical for Nickel Chromium Molybdenum Steel |
ASTM A534 Grade 4320H electrical
| Property |
Value |
| Aluminium |
Aluminium of 0.05 % |
| Carbon |
Carbon of 0.17 - 0.23 % |
| Chromium |
Chromium of 0.35 - 0.65 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.4 - 0.7 % |
| Molybdenum |
Molybdenum of 0.2 - 0.3 % |
| Nickel |
Nickel of 1.55 - 2 % |
| Oxygen |
Oxygen of 2E-3 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.015 % |
ASTM A534 Grade 4320H mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Nickel Chromium Molybdenum Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Nickel Chromium Molybdenum Steel |