ASTM A515 Grade 70
ASTM A515 Grade 70 introduction
Steel for pressure vessels and boilers differ from other carbon-manganese structural steels due to their high resistance to pressure at all temperatures (ambient, low or high).
The fundamental property of steels for pressure vessels is their ability to withstand high pressure at different temperatures. They have good weldability, as well as excellent toughness, and are suitable for normalisation annealing and stress-relief annealing (both treatments neutralise local hardening caused by welding).
ASTM A515 Grade 70 general
| Property |
Value |
Comment |
| Elongation |
Elongation of 17 % |
min. | for thickness 5-80 mm | A8 | Transverse |
| - |
Elongation of 21 % |
min. | for thickness 5-80 mm | A2 | Transverse |
| Tensile strength |
Tensile strength of 485 - 620 MPa |
for thickness 5-80 mm | Transverse |
| Yield strength |
Yield strength of 260 MPa |
min. | for thickness 5-80 mm | Transverse |
ASTM A515 Grade 70 thermal
| Property |
- |
- |
| Application areas |
| Delivery condtion |
| Other |
ASTM A515 Grade 70 mechanical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.31 % |
max. | for thickness 5-25 mm |
| - |
Carbon of 0.33 % |
max. | for thickness 25-50 mm |
| - |
Carbon of 0.35 % |
max. | for thickness 50-80 mm |
| Manganese |
Manganese of 1.2 % |
max. | for thickness 5-80 mm |
| Phosphorus |
Phosphorus of 0.025 % |
max. | for thickness 5-80 mm |
| Silicon |
Silicon of 0.15 - 0.4 % |
for thickness 5-80 mm |
| Sulfur |
Sulfur of 0.025 % |
max. | for thickness 5-80 mm |