ASTM A414 Grade C Hot-Rolled
ASTM A414 Grade C Hot-Rolled general
| Property | Temperature | Value |
|---|---|---|
| Elongation A200 | 23.0 °C | Elongation A200 of 16 % |
| Elongation A50 | 23.0 °C | Elongation A50 of 19 - 22 % |
| Tensile strength | 23.0 °C | Tensile strength of 380 - 485 MPa |
| Yield strength | 23.0 °C | Yield strength of 230 MPa |
ASTM A414 Grade C Hot-Rolled mechanical
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.02 - 0.08 % |
| Carbon | Carbon of 0.25 % |
| Chromium | Chromium of 0.3 % |
| Copper | Copper of 0.4 % |
| Manganese | Manganese of 0.9 % |
| Molybdenum | Molybdenum of 0.12 % |
| Nickel | Nickel of 0.4 % |
| Niobium | Niobium of 0.02 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 0.3 % |
| Sulfur | Sulfur of 0.035 % |
| Titanium | Titanium of 0.03 % |
| Vanadium | Vanadium of 0.03 % |