ASTM A372 Grade P Class 100, Liquid Quenched and Tempered, or Normalized followed by Liquid Quench and Temper
ASTM A372 Grade P Class 100, Liquid Quenched and Tempered, or Normalized followed by Liquid Quench and Temper general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A372 Grade P Class 100, Liquid Quenched and Tempered, or Normalized followed by Liquid Quench and Temper thermal
| Property | Value |
|---|---|
| Carbon | Carbon of 0.4 % |
| Chromium | Chromium of 2.3 - 3.3 % |
| Manganese | Manganese of 0.9 % |
| Molybdenum | Molybdenum of 0.8 - 2 % |
| Nickel | Nickel of 0.35 % |
| Phosphorus | Phosphorus of 0.02 % |
| Silicon | Silicon of 0.02 % |
| Vanadium | Vanadium of 0.3 - 0.5 % |
ASTM A372 Grade P Class 100, Liquid Quenched and Tempered, or Normalized followed by Liquid Quench and Temper mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 16 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 248 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Tensile strength | 23.0 °C | Tensile strength of 795 - 965 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 690 MPa | - |