ASTM A336 Grade F92 Normalized and Tempered or Liquid Quenched and Tempered
Equivalent material: ASTM Grade T92, UNS K92460
ASTM A336 Grade F92 Normalized and Tempered or Liquid Quenched and Tempered general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A336 Grade F92 Normalized and Tempered or Liquid Quenched and Tempered thermal
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.02 % |
| Boron | Boron of 1E-3 - 6E-3 % |
| Carbon | Carbon of 0.07 - 0.13 % |
| Chromium | Chromium of 8.5 - 9.5 % |
| Manganese | Manganese of 0.3 - 0.6 % |
| Molybdenum | Molybdenum of 0.3 - 0.6 % |
| Nickel | Nickel of 0.4 % |
| Niobium | Niobium of 0.04 - 0.09 % |
| Nitrogen | Nitrogen of 0.03 - 0.07 % |
| Phosphorus | Phosphorus of 0.02 % |
| Silicon | Silicon of 0.5 % |
| Sulfur | Sulfur of 0.01 % |
| Titanium | Titanium of 0.01 % |
| Tungsten | Tungsten of 1.5 - 2 % |
| Vanadium | Vanadium of 0.15 - 0.25 % |
| Zirconium | Zirconium of 0.01 % |
ASTM A336 Grade F92 Normalized and Tempered or Liquid Quenched and Tempered mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 20 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Reduction of area | 23.0 °C | Reduction of area of 45 % | - |
| Tensile strength | 23.0 °C | Tensile strength of 620 - 830 MPa | - |
| Yield strength | 23.0 °C | Yield strength of 440 MPa | - |