ASTM A311 Grade 1541 Normal Draft Cold Drawn and Stress Relief Annealed

Equivalent material: DIN 1.1127, DIN 38Mn6, AFNOR 38Mn6, BS 38Mn6, AISI 1541, SAE 1541, JIS SMn438, JIS SMn438H, JIS SMn438M, EN 38Mn6, EN 1.1127, GOST 40G2, GB/T 40Mn2, GB/T A00402, ASTM 1541, UNS G15410, IS SMn438

ASTM A311 Grade 1541 Normal Draft Cold Drawn and Stress Relief Annealed general

Property Temperature Value Comment
Density 23.0 °C Density of 7.8 - 7.9 g/cm³ Typical for Medium Carbon Steel

ASTM A311 Grade 1541 Normal Draft Cold Drawn and Stress Relief Annealed thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.32E-5 1/K Typical for Medium Carbon Steel
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1380 - 1514 °C Typical for Medium Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 470 - 520 J/(kg·K) Typical for Medium Carbon Steel
Thermal conductivity 23.0 °C Thermal conductivity of 21 - 52 W/(m·K) Typical for Medium Carbon Steel

ASTM A311 Grade 1541 Normal Draft Cold Drawn and Stress Relief Annealed magnetic

Property Value
Carbon Carbon of 0.36 - 0.44 %
Manganese Manganese of 1.35 - 1.65 %
Phosphorus Phosphorus of 0.04 %
Sulfur Sulfur of 0.05 %

ASTM A311 Grade 1541 Normal Draft Cold Drawn and Stress Relief Annealed electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m Typical for Carbon Steel

ASTM A311 Grade 1541 Normal Draft Cold Drawn and Stress Relief Annealed mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 200 - 215 GPa Typical for Medium Carbon Steel
Elongation A50 23.0 °C Elongation A50 of 10 - 11 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Medium Carbon Steel
Reduction of area 23.0 °C Reduction of area of 30 - 35 % -
Shear modulus 23.0 °C Shear modulus of 75 - 80 GPa Typical for Carbon Steel
Tensile strength 23.0 °C Tensile strength of 585 - 690 MPa -
Yield strength 23.0 °C Yield strength of 520 - 620 MPa -

Contact us

Henan Bebon Iron&Steel Co., Ltd.

Xicheng Science & Technology Building High-tech Development Zone, Zhengzhou, China

Tel: +86-371-86151827

E-Mail: [email protected]

PlaceholderContact us

Message