ASTM A276 Grade S32654 Annealed; Hot-Finished or Cold-Finished
Equivalent material: DIN 1.4652, AISI S32654, SAE S32654, EN X1CrNiMoCuN24-22-8, EN 1.4652, UNS S32654
ASTM A276 Grade S32654 Annealed; Hot-Finished or Cold-Finished general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A276 Grade S32654 Annealed; Hot-Finished or Cold-Finished thermal
| Property | Value |
|---|---|
| Carbon | Carbon of 0.02 % |
| Chromium | Chromium of 24 - 25 % |
| Manganese | Manganese of 2 - 4 % |
| Molybdenum | Molybdenum of 7 - 8 % |
| Nickel | Nickel of 21 - 23 % |
| Nitrogen | Nitrogen of 0.45 - 0.55 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.5 % |
| Sulfur | Sulfur of 5E-3 % |
ASTM A276 Grade S32654 Annealed; Hot-Finished or Cold-Finished mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 40 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 250 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Reduction of area | 23.0 °C | Reduction of area of 40 % | - |
| Tensile strength | 23.0 °C | Tensile strength of 750 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 430 MPa | - |