ASTM A276 Grade N08367 Annealed; Hot-Finished or Cold-Finished
ASTM A276 Grade N08367 Annealed; Hot-Finished or Cold-Finished general
| Property | Temperature | Value |
|---|---|---|
| Elongation A50 | 23.0 °C | Elongation A50 of 30 % |
| Reduction of area | 23.0 °C | Reduction of area of 50 % |
| Tensile strength | 23.0 °C | Tensile strength of 655 MPa |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 310 MPa |
ASTM A276 Grade N08367 Annealed; Hot-Finished or Cold-Finished mechanical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.03 % |
| Chromium | Chromium of 20 - 22 % |
| Manganese | Manganese of 2 % |
| Molybdenum | Molybdenum of 6 - 7 % |
| Nickel | Nickel of 23.5 - 25.5 % |
| Nitrogen | Nitrogen of 0.18 - 0.25 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.03 % |