ASTM A276 Grade 414 Hardened and tempered at a relatively high temperature; Hot-Finished or Cold-Finished
Equivalent material: AMS 5615, ASTM MT414, UNS S41400
ASTM A276 Grade 414 Hardened and tempered at a relatively high temperature; Hot-Finished or Cold-Finished general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A276 Grade 414 Hardened and tempered at a relatively high temperature; Hot-Finished or Cold-Finished thermal
| Property | Value |
|---|---|
| Carbon | Carbon of 0.15 % |
| Chromium | Chromium of 11.5 - 13.5 % |
| Manganese | Manganese of 1 % |
| Nickel | Nickel of 1.25 - 2.5 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.03 % |
ASTM A276 Grade 414 Hardened and tempered at a relatively high temperature; Hot-Finished or Cold-Finished mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 15 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Reduction of area | 23.0 °C | Reduction of area of 45 % | - |
| Tensile strength | 23.0 °C | Tensile strength of 790 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 620 MPa | - |