ASTM A240 Grade S35315 Heat-Treated
Equivalent material: DIN 1.4854, DIN X6NiCrSiNCe35-25, AISI S35315, SAE S35315, EN X6NiCrSiNCe35-25, EN 1.4854, UNS S35315
ASTM A240 Grade S35315 Heat-Treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A240 Grade S35315 Heat-Treated thermal
| Property | Value |
|---|---|
| Carbon | Carbon of 0.04 - 0.08 % |
| Chromium | Chromium of 24 - 26 % |
| Manganese | Manganese of 2 % |
| Nickel | Nickel of 34 - 36 % |
| Nitrogen | Nitrogen of 0.12 - 0.18 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1.2 - 2 % |
| Sulfur | Sulfur of 0.03 % |
ASTM A240 Grade S35315 Heat-Treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 40 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 217 [-] | - |
| Hardness, Rockwell B | 23.0 °C | Hardness, Rockwell B of 95 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Tensile strength | 23.0 °C | Tensile strength of 650 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 270 MPa | - |