ASTM A234 Grade WP9 CL1 Heat-Treated
ASTM A234 Grade WP9 CL1 Heat-Treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A234 Grade WP9 CL1 Heat-Treated thermal
| Property | Value |
|---|---|
| Carbon | Carbon of 0.15 % |
| Chromium | Chromium of 8 - 10 % |
| Manganese | Manganese of 0.3 - 0.6 % |
| Molybdenum | Molybdenum of 0.9 - 1.1 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.03 % |
ASTM A234 Grade WP9 CL1 Heat-Treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | Typical for Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 14 - 22 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Tensile strength | 23.0 °C | Tensile strength of 415 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 205 MPa | - |